Electrostatic spray thermosetting RAL Color Powder Coating

electrostatic spray thermosetting RAL Color Powder Coating

Used for:To electrostatic spray all metal products as follows,
Powder Coating for Steel/Gavalized Steel Products
Powder Coating for Iron Products
Powder Coating for Aluminium Products

Curing information:
Normal curing is as follows,
For outdoor use:200degree/10minutes
For indoor use:180degree/15minutes

Basic information:
Hardness:1H-2H
Adhensive:0 class
Impact:50kgs
Gloss:5%-100%

 

Powder Coating:

Metal Powder Coating

Metal Door Powder Coaitng

Metal Funiture Powder Coating

Metal Rack Powder Coating         

Storage Rack Powder Coating

Aluminium Profile Powder Coating

Aluminum Profile Powder Coating

Electric Cabinet Powder Coating

Electric Fan Powder Coating

 

Finish include:

Sand texture, hammer texture, silk pattern,lizard texture, sand textured, ,metallic,smooth glossy/matt,transparent clear,mirror chrome silver and so on

 

AVERAGE COVERAGE 

8-12 square meters / kg, thickness 60 microns (100% of the powder coating utilization rate)

PACKING

Outside carton lined with two layers of polyethylene bags, each containing 20kg or 25 kg net weight.

 

PHYSICAL PROPERTIES

• Specific gravity : 1.2 ~ 1.8g/cm3 up to colors
• Particle size distribution: 100% less than 100 microns (depending on the specific indicators art effects may be, according to the special requirements of painting adjusted)
• Level of liquidity: 24 ~ 27 mm

 

 

Mechanical property
Testing items	Standards and methods	Inspecting index
impact	GB/T1732-1993, AS3715 2.8	>50kg/cm
Bending	GB/T1185-88, AS1580 402.1, ISO9227	3mm
Adhesion CHECKED TEST	GB/T9286-88,2mm Cross cut, ISO2409	0 class
Cupping	Erichsen, ISO1520	6mm
Pencil hardness	GB/T6739-86, Mitsubishi	Pass H-2H
Chemical resistance and weather resistance
Salt spray test	GB/T1771-91,500 hours	The cross section of corrosion less than 2MM
Hot and damp resistance test	GB/T17740-79(89),1000 hours	Without air bubbles, loses the light slightly
Acid resistance	10% CH3COOH, 240 hours	Without air bubbles, the surface without damage
Alkali resistance	10% NaOH, 240 hours	Without air bubbles, the surface without damage
Heat resistance	200degree,1 hour	The color change is lower than E=1.5
Solvent resistance	MEK24 hours soaked in solvent-free	Without air bubbles, the surface without damage
Uvioresistant	QUV-313,500 hours	Gloss higher than 80% lower than the  Munsell color change level
Water tolerance of	2 hours	No bubble, not falling, losing light